EL-Lene H1000PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. EL-Lene H1000PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.
Melt Flow RateISO 1133 @ 190oC, 5.0 kg0.25g/10 min
| Property | Test Method | Typical Value | Unit |
| Density (Compound) | ISO 1183 | 0.959 | g/cm3 |
| Tensile Strength at Yield | ISO 527 @ Crosshead speed 100 mm/min | 23 | Mpa |
| Tensile Strength at Break | ISO 527 @ Crosshead speed 100 mm/min | >30 | Mpa |
| Elongation at Break | ISO 527 @ Crosshead speed 100 mm/min | >600 | % |
| Carbon Black Content | ISO 6964 | 2.25 | % wt |
| Carbon Black Dispersion | ISO 18553 | <3 | – |
| Oxidative induction time | NF EN 728 @ 200oC | >60 | min. |
| Flexural Modulus | ASTM D 790 | 1000 | MPa |
| Hardness | ASTM D 2240 | 64 | Shore D |
| ESCR | ASTM D 1693 | >10000 | Hrs, F0 |
| Resistance to slow crack growth | ISO 13479 @ 80oC | >500 | Hrs |
| Rapid crack propagation | ISO 13477) | >10 | bar |
| Resistance to gas constituents | ISO 1167 | >20 | Hrs |