| Property | Test Method | Typical Value | Unit |
| Melt Flow Rate | ASTM D 1238 @190oC, 2.16Kg | 0.4 | g/10 min |
| HLMI | ASTM D 1238 @190oC, 21.6Kg | 40 | g/10 min |
| DENSITY | ASTM D 1505 | 0.955 | g/cm3 |
| Melting point | ASTM D 2117 | 132 | oC |
| Vicat softening point | ASTM D 1525 | 128 | oC |
| Brittlness Temperature | ASTM D 746 | <-60 | oC |
| Tensile strength at yeild | ASTM D 638 | 280 | Kg/cm2 |
| Tensile strength at break | ASTM D 638 | 350 | Kg/cm2 |
| Elongation at break | ASTM D 638 | 1000 | % |
| Flexural modulus | ASTM D 790 | 12000 | Kg/cm2 |
| Notched izod impact | ASTM D 256 @190oC | 98 | j/m |
| ESCR | ASTM D 1693 @50oC | 300 | Hrs, F50 |