These grades are suitable for rotational moulding of storage tanks and general purpose applications.
| Property | Test Method | Typical Value | Unit |
| Resin Properties | |||
| Melt Flow Rate | ASTM D 1238 @ 190 °C, 2.16 kg | 4 | g/10 min |
| Density | ASTM D 1505 | 0.938 | g/cm3 |
| Melting Point | <3 | 125 (257) | °C (°F) |
| Crystallization Point | ASTM D 2117 | 113 (236) | °C (°F) |
| Heat Deflection Temperature | ASTM D 648 @ 0.455 Mpa | 65 (149) | °C (°F) |
| Vicat Softening Temperature | ASTM D 1525 | 116 (241) | °C (°F) |
| Mechanical Properties | |||
| Tensile Strength-at-Yield | ASTM D 638 @ Speed 50 mm/min | 20 (2900) | MPa (psi) |
| Tensile Strength-at-Break | ASTM D 638 @ Speed 50 mm/min | 18 (2600) | MPa (psi) |
| Elongation-at-Break | ASTM D 638 @ Speed 50 mm/min | 800 | % |
| Flexural Modulus | ASTM D 790 | 700 (102000) | MPa (psi) |
| Surface Hardness | ASTM D 2240 | 60 | Shore D |
| ARM Impact Strength @ -40 °C | ARM Method (5.5 mm rotomoulded sample) | 27 (110) | J/mm (lb-ft) |
| Brittleness Temperature | ASTM D 746 | < -60 (-76) | °C (°F) |